CiM colour testing: Velveteen, Toto, Allspice

These were the new CiM limited edition colours out in spring 2016. I am somewhat behind on writing this post as Flame Off happened…

Also, I got into fountain pens recently, and decided to use my post to practise my italic handwriting so that I got both the thing I had to do and the thing I wanted to do done. Pics thereof at the bottom.

Velveteen

This is a pale peachy brown opalino that can develop mottled striations on the surface. I made four spacers and etched two of them; they do etch and it makes the striations more visible.

16.03.12_Velveteen_spacers

I made a pair of rounds with 006 clear cores. One has a band of silvered ivory around the centre, and the other has a couple of wraps of fine silver wire, melted in so it balls up. There’s a bit of brown fuming from the silver – not a huge amount. The SIS wrap has a clearly demarcated edge and has not spread a great deal.

16.04.10_Velveteen_SISsilver

I made a sculptural gremlin (with bunny ears – could do with a redesign!) with a clear core. It is opaque enough not to have the teeth show through the lips, which is a disconcerting look when it happens. The striations are easiest to see on the body, which is worked longest, but there are also a couple of larger dark areas on the ears.

16.03.29_Velveteen_gremlin

I did a little silver glass testing. First is a bead with a clear core, encased in Velveteen, with a stripe of Double Helix boreas. This was reduced (oxy down) and encased. There’s some darker brown fuming and the boreas is a lovely bright iridescent purple with some mottling.

The second silver glass bead has okeanos instead, again reduced. It has ended up with a variety of colours, from yellow-green to light turquoise to deep blue, again with interior mottling. The stripe has remained thin and not expanded. In the centre of the bead, there is a pronounced dark line at the edge of the silver glass, bordered with a light greenish and the deep blue pushed into the centre of the stripe.

16.04.10_Velveteen_okeanosboreas

Toto

Toto is a soft milky brown with a touch of grey. My spacers came out a uniform colour. The etched pair look softer and lighter.

16.03.12_Toto_spacers

This pair of rounds have cores of 006 clear encased in Toto. One has a wrap of silvered ivory stringer which has spread and fuzzed at the edges. The surface has some darker grey areas. The second bead has two wraps of fine silver wire around the centre, melted in. It has fumed a dark brown line where the silver has melted in.

16.04.10_Toto_SISsilver

My sculptural gremlin is a fairly uniform colour on the front – it has some of the darker grey visible on the back and the soles of the feet, which are cooled swiftly when I flatten them.

16.03.29_Toto_gremlin

Silver glass beads: core of clear, encased in Toto, spiral of silver glass which is reduced and encased in clear. The first bead uses boreas, which has not come out well – it is mostly a greenish brown with only the slightest patch of iridescent purple. The base is visible as a dark brown next to the boreas. The okeanos came out much better and has struck to blue-purples with green at the ends. The Toto shows through as a warmer brown with separation lines where it meets the okeanos.

16.04.10_Toto_okeanosboreas

Allspice

Allspice is a fairly dark amber brown opalino. Used on its own, the spacers are a lovely warm and deep colour. The etched spacers have a nice inner glow.

16.03.12_Allspice_spacers

The pair of rounds with cores of 006 clear and surface decoration have a wrap of silvered ivory stringer and a couple of wraps of fine silver wire. The SIS has not spread much and has sharply defined edges. The silver has a small dark outline immediately adjacent. These beads both have some mottling in the surface of the Allspice. (So do the spacers a little, but it isn’t so evident to the naked eye).

16.04.10_Allspice_SISsilver

In my sculptural gremlin, the Allspice is just thick enough for the white of the teeth not to show through. There is only visible surface mottling on the back.

16.03.29_Allspice_gremlin

In my silver glass beads, the wraps did not spread and the edges and swallowed, giving very narrow bands. These beads have a core of clear, encased in Allspice, a spiral of silver glass, reduced and encased in clear. The Allspice has visible mottling. The boreas has a shiny band of purple surrounded by a darker brown – the same colour as the mottles. The okeanos has narrow very dark edges surrounding the centre stripe with ranges from brighter to darker blue, with some lime green near the holes.

16.04.10_Allspice_okeanosboreas

Handwriting

For anyone interested in fountain pens.
Here is my normal handwriting, where I composed the text. I can write reasonably straight without guides.

16.05.27_planning

16.05.27_planning_02

These were written with a recently-acquired Osmiroid 75 fountain pen with an italic extra fine straight nib. The ink is whatever was in the pen – I’d just added enough water to get it going and decided to write it empty because I just discovered piston fillers take forever to clean out by sucking up and expelling water… You can see it ran out during the third composition – I’d added more water but it was too faint by then so I finished cleaning it.

Here’s the first go – this was still with the old ink. I’d printed out some guide paper and this was the first time I’d used it. I was trying to get it all on one sheet (and failed) hence the lack of paragraph spacing. I was also putting one letter in each grid box, meaning my spacing is rather odd – the ‘m’s are very squished and some words are over-expanded. I used this calligraphy paper PDF generator printed out on my normal printer paper.

16.05.27_Velveteen_italic

I aso realised I hadn’t practised capitals at all…

Second post: ink had run out so I refilled with Diamine indigo. The two look closer in the pics than they should – the original ink was a nice blue/blue-black and indigo has more of a steel grey tint in it. This time I used slightly smaller paper – 0.5 rather than 0.6mm nib size, and with halfway vertical guides too. I mostly ignored the guide boxes this time, just using them to go vaguely in the right direction and not for spacing. Also less obvious in the photo, it starts out with wetter writing so the letters are darker, then for the rest my writing angle must have changed, as I have drier writing and it also gets bigger. That was partly the fault of writing without bright enough light coming from the right direction, as I couldn’t always see the guidelines… The part at the bottom is darker and smaller again. I couldn’t work out how to write the correct s at that size – it’s supposed to be a narrow letter and it was very difficult not to write it wider.

16.05.29_Toto_italic

Third: I went back to the bigger size but kept the extra verticals. It’s looking a bit better, though still various irregularities.

16.06.04_Allspice_italic

Some practise, may also show the ink colour difference a little.

16.05.27_Velveteen_italic_02

Big practice, back with the Lamy Joy and 1.9mm nib. I managed the s shape once or twice at this size!

16.05_practise

, , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , , ,

Leave a comment

CiM colour testing: Indian Summer, Dirty Laundry and a little more Ogre

Indian Summer

Indian Summer is an interesting one – it’s a striking amber.

15.10.05_Indiansummerstriking

I took an on-mandrel pic to show the striking.

15.10.05_indiansummer_dirtylaundry_spacers

Here are Indian Summer and Dirty Laundry spacers. Indian Summer didn’t etch particularly consistently – the very dark bead appeared to etch more. Dirty Laundry is an opal white, and looks as expected here.

I expected both of these colours to be reactive so had hope for the silver glass results.

15.10.18_indiansummer_luna_boreas

The bead on the right here shows that Indian Summer is not good as a surface encasing colour – it just gets too dark, especially as this bead had a core of Indian Summer as well. The silver glass in that one was Luna 2.1 which is mostly transparent and you can just see some streaks round the middle. The other two beads had a core of 006 clear, encased in Indian Summer, then Luna 2.1 scrolls on the left and Boreas dots in the centre bead. Both promising: the Luna 2.1 scrolls have sharp light edges in some places and fuzzier edges but a defined centre in others – those are the purpler more transparent areas. The Boreas dots have a concentrated very shiny centre, then a ring where it appears the Indian summer has displaced it, then an outer ring which has a shiny area and then a dark sharp outer line.

15.11.07_indiansummer_luna_boreas_01

I then did a pair which have an Indian Summer core, a spiral of silver glass and encased in 006. Very interesting! Boreas is on the left – the core looks extremely dark and the boreas is a dark blue with bright green edges fading to brown. (Ignore the grey bubbles at the bottom – the end of my clear was dirty and I didn’t notice until too late).

15.11.07_indiansummer_luna_boreas_02

The Luna 2.1 bead (right) is the usual pinky-purple and has developed blue-green lines and haze in the centre of each spiral. The edges of the spiral are the lighter amber areas.

Dirty Laundry

15.10.07_dirtylaundry_luna_boreas

Luna 2.1 scrolls on the left, Boreas dots on the right. Both colours get some slight outlining effects, but what is most interesting is the different ways the base has fumed in each case. Under the Boreas, the Dirty Laundry has gone a cold yellow-green, while under the Luna 2.1 it has flushed a warm colour. (Boreas isn’t a great colour to put over pale white or tan opaques because as a transparent purple it will always show brownish).

These next two are fabulous though.

15.11.07_dirtylaundry_luna_boreas_01

These are both encased in 006. The silver glass in both cases has a mottled and feathered look with noticeable edges. The Boreas on the right is blue-purple and the Dirty Laundry underneath has fumed a darker caramel brown. The Luna 2.1 bead on the left is lovely. The silver glass has again formed dark then light lines in the centre, and the darker amber lines are the gaps between the spirals. The Dirty Laundry hasn’t fumed very far though, leaving cloudy white ends which I love.

15.11.07_dirtylaundry_luna_boreas_02

Here you can see the Dirty Laundry parts of the Boreas bead – they have still fumed somewhat tan and have darker outlines rather than the fuzzy ones with the Luna 2.1.

Ogre

Finally, a silver glass pair on Ogre.

15.10.07_ogre_luna_boreas

Luna 2.1 scrolls and Boreas dots, as before. You can see slight separation lines around the edges of the scrolls, and the Boreas dots are again very shiny and have sharp brown rings around them. Around the beadholes has also tended to go brown. Quite interesting for organic beads.

, , , , , , , , , , , , , , , ,

Leave a comment

CiM colour testing: Charlotte and Limelight

These are both very pretty transparents.

Limelight is a clean, cool green with no hints of yellow. Charlotte is a warm pink that is saturated enough to hold its own. I don’t think we’ve had anything else in 104 quite this colour (not counting CiM’s Paris, out at the same time and very similar). Both have a tendency to develop microbubbles, especially Charlotte – if you heat them further out they may get fewer.

15.10.05_limelightcharlotte_spacers

(The last Charlotte spacer was half out of the etching liquid on this side – I left it like this because I liked it).

15.10.05_charlotte_comparison

Here’s a comparison with a couple of other pinks I had to hand – Lauscha transparent pink is a baby pink and cooler in tone than Charlotte. I think the very pale one is Effetre rose quartz 067 – it is definitely Effetre, and their transparent pink tends to be a little peachier most of the time. You can see how well the colour shows in the etched Charlotte. I’d call this a cherry blossom colour. (The dark violet is just there because it was on the same string as the pink).

I then tried encasing silver glass with these transparents. I’ve been using Boreas for this for a while – it is a transparent reducing purple. This time I also added Luna 2.1 which is a mostly transparent striking colour.

15.10.05_limelight_lunaboreas_01

This is a core of clear encased in Double Helix Luna 2.1 (left) and Boreas (middle and right) encased with limelight. I did two with the boreas because I had an insufficient reduction moment with the middle bead. The limelight is pale enough that you don’t notice it much. There’s some good electric blue from the boreas on the right, and you can see the range of striking that Luna gets, from opaque yellow to transparent pinky purple. Probably not the best use for limelight, just because you can’t really tell it is there and it doesn’t appear to be affecting the silver glass.

15.10.05_limelight_lunaboreas_02

Above is a second view of the limelight beads.

15.10.18_charlotte_luna_boreas

I did the same thing with Charlotte – this time I did two Boreas beads because the thicker encasing on the rightmost bead just ended up a murky green-brown. The middle bead has a thinner encasing and you can see some hints of pink at the top, while over the most reduced areas it is still the weird greenish colour. Silver tends to fume pinks brown – I don’t think I’ve ever tried similar with a transparent pink before. Luna 2.1 on the left is a better match – the pretty pink wisps inside go with the encasing. On the whole, you probably want this glass to look like itself rather than use it with silver glass though. (You can also see some areas of the microbubbles on these beads – once they’re there, you can’t get rid of them).

, , , , , , , , , , , , ,

Leave a comment

%d bloggers like this: