A couple more comparisons between the limited edition colours.
Green Lantern is greener than absinthe or aloe juice, which are bluer. (Doesn’t show up so well here, but by eye it is). Aloe juice is also less saturated.
Marine is partway between trade winds and tuscan teal – it’s greener and lighter than trade winds but bluer than tuscan teal. None of them are anywhere near as dark as leaky pen.
With the opaque greens, I have included cardamom and Effetre grasshopper green. It Ain’t Easy Being is very much bluer, cardamom is heading more towards the lime end, mint chip is muted and grasshopper green is more saturated. The CiM greens can kind of give the same impression when you look at them one at a time, but they’re definitely different when side-by-side.
To test the striking colours in circumstances where they’re more likely to strike, I made pressed lentil beads.
Radio Flyer: definitely opaque-looking.
Bing: has opacified a bit more. You can see the mandrel hole, but I’d list this as semi-opaque.
Absinthe: still very transparent.
Tandoori: has struck much oranger and has gone cloudy. (Though slightly unevenly at one end, which is lighter than the other). I also did a bead with psyche scrolls on tandoori – the psyche shows up as dark blue with plenty of shine and the tandoori has darkened more.
Here’s a close up of the tandoori beads.
Next I tested mint chip with copper green and psyche.
The mint chip has gone a bit streaky under both of these, but more so with the psyche. The copper green has done its thing where it goes darker in the centre with a pale halo, but it has also greyed up a great deal. Psyche has fumed the base yellow and is showing up as brownish purple. That’s fairly expected.
Here is psyche on the other neutrals.
Cake batter has stayed very clean-looking and has only been fumed a very small amount. The psyche appears very brown.
Antique Lace is a bit streaky, has stayed a pinkish brown and the psyche is fairly brown.
Muskmelon has gone streakier and fumed darker, and the psyche has blue hints. This seems the most reactive base out of the three.
I have some CiM to test!
This is the first half, covering the greens and blues. The next lot are reds, oranges, pinks and neutralish colours.
Here are the transparent/translucent greens and blues in rod form.
Front to back: aloe juice, absinthe, Tuscan teal, trade winds and neon blue.
These are the opaque green rods.
Goblin, shrubbery and mint chip.
I mostly did small plain beads for this pass of testing, just to see how the colours came out and how they were to work.
Aloe juice and absinthe
In small spacers, they looked very similar. Aloe juice is a very pretty transparent green, nice to work. Absinthe is an opal/translucent and it appears it takes a bit of effort to make it do that. It has the slightest hint of mistiness in the spacers I made, and is a tiny bit darker than the aloe juice, though that is more obvious when both are larger. Absinthe is also a much softer colour that likes to spread along the mandrel. It either doesn’t etch at all, or needs a lot longer in the etching liquid. The little spacer at the end was the etch attempt. Aloe juice etches well for a sea-glass look.
Tuscan teal and trade winds
Tuscan teal is a lovely deep teal, not too green, and is not so dark that you can’t use it on its own in spacers, but also looks great over white. (I am using Effetre white in all these). Etches fine. Trade winds is a very dark midnight denimy blue. I didn’t do plain spacers with this, they would have just looked dark. Again, looks great over white and etches.
Neon blue is similar to cobalt, but is a slightly different shade. It is surprisingly soft for such a saturated blue. Etching makes it seem very slightly purpler. It stands out very well on top of white. I am keeping an eye on these because one of the ones over white has a crack, but there was also a brief power cut when the kiln had nearly finished ramping down, so I can’t be certain if there’s any problem there. The second bead has no cracks yet, and I did an unphotographed test of it over CiM peace the next day too.
Mint chip, shrubbery and goblin
I like these greens sitting side by side like this! Mint chip is a beautiful pale opaque green. There have been a few of these from CiM with slightly different shades – sprout, for example, and I don’t have them side-by-side to compare right now. Mint chip goes by its name well – it is a pretty minty green, no yellow tinge. It also has a very smooth uniform colour, no darker lines.
Shrubbery is a mid, yellowish green. I wouldn’t quite call it an olive, but it’s getting there. It does have noticeable lines where the colour has been applied.
I like goblin a lot. It is a dark olive colour with dark lines that is deep and shiny on its own and softer when etched. Good for organics and leaf tones, I would think! The rod was a bit shocky though – if you look up at the rod photo, you can see it’s cracked just above the dark line where the most heated section stopped. When I was doing my sculptural bead below, I had to baby it back into the flame every time I picked it up again, or it was shocking off along there and losing a significant chunk of glass. I only had the one rod, so I can’t say whether this would happen with all of them.
Here’s a pic on side so you can see the streakiness or lack thereof better.
Then I had some fun and made some goblin beads! (Using my dragon eye murrini). These are grumpier than gremlins and have much bigger TEETH.
Goblin, shrubbery and Weimaraner (of which more next time). The colours are darker in places when worked like this: they go in and out of the flame a lot and have heat directed at specific areas, which brings out the darker lines. You can see a little bit of reduction here and there, particularly near goblin goblin’s eye. I like the gnarly look on these!